HARDOX600耐磨钢板厂家:什么可以较少对于钢的凿削磨损程度

所属分类:常见问题 发布时间:2021-04-15 17:15:47 来源:http://www.lcnmb500.com 浏览量:

在非强冲击磨料磨损工作条件下,hardox400耐磨板的耐磨性与碳含量的关系。从试验中可以看出,随着碳含量的提高,耐磨板的耐磨性提高。这是因为碳的固溶强化作用可以减少磨料对钢的凿削磨损。

The relationship between the wear resistance and carbon content of Hardox400 wear-resistant plate was studied under the condition of non strong impact abrasive wear. It can be seen from the test that with the increase of carbon content, the wear resistance of the wear plate is improved. This is because the solid solution strengthening effect of carbon can reduce the gouging wear of abrasive on steel.

 HARDOX600耐磨钢板厂家:什么可以较少对于钢的凿削磨损程度(图1)

另外,当碳含量的提高超出一般范围时,即使经过常规固溶处理,也容易在钢中残存一部分弥散分布的碳化物。这种组织有利于提高非强冲击磨料磨损条件下工件的耐磨性。钢中碳含量较高而锰含量较低时,也容易出现这种碳化物。

In addition, when the increase of carbon content is beyond the general range, even after conventional solid solution treatment, it is easy to retain some dispersed carbides in the steel. This kind of structure is beneficial to improve the wear resistance of the workpiece under the condition of non strong impact abrasive wear. When the carbon content in steel is high but the manganese content is low, this kind of carbide is easy to appear.

碳含量可以选择在1.25%以上。但在强冲击条件下,这种提高碳含量的措施并不能保证提高耐磨性。因此,这种关系只是在一定条件下是正确的。

The carbon content can be more than 1.25%. But under the condition of strong impact, this measure of increasing carbon content can not guarantee the improvement of wear resistance. Therefore, this relationship is correct only under certain conditions.

HARDOX悍达600是世界上硬的耐磨钢板,硬度值达是600HBW。它一般应用于磨损极其严重的场合,并且主要用来替代铸钢、铬合金铸铁以及表面硬化金属。尽管它的硬度很高,我还是能够对它进行机加工、焊 接和切割。尽管HARDOX悍达600的硬度非常高,但它仍具有相当高的冲击韧性。

HARDOX 600 is the world's hard wear-resistant steel plate, hardness value is 600hbw. It is generally used in the situation of severe wear, and mainly used to replace cast steel, chromium alloy cast iron and surface hardening metal. Despite its high hardness, I was able to machine, weld and cut it. Although HARDOX 600 has a very high hardness, it still has a very high impact toughness.