hardox耐磨板按硬度等级分为:hardox400、hardox450、hardox500、hardox550、hardox600。这意味着您总能找到一种满足您的特定需求的hardox450耐磨板。

HARDOX wear-resistant plates are divided into Hardox400, hardox450, hardox500, hardox550 and hardox600. This means that you can always find a hardox450 wear plate that meets your specific needs.

hardox400耐磨板和hardox450是多用途的耐磨板。由于其高韧性、良好的弯曲和焊接性能,在一些应用中也可用作承载用途。

Hardox400 wear plate and hardox450 wear plate are multi-purpose wear plate. Because of its high toughness, good bending and welding properties, it can also be used as load-bearing in some applications.

hardox500是一种可弯曲和焊接的耐磨板,可应用于对耐磨性能要求更高的领域。

Hardox500 is a kind of bending and welding wear-resistant plate, which can be used in the field with higher requirements for wear resistance.

hardox450是一种平均硬度为450HBW的耐磨钢板,其韧性与hardox500相同,被应用于高磨损的场合。其主要针对使用高锰钢铸件或布氏硬度为500的耐磨钢板的用户和制造商。当从hardox500钢板升级到该产品时,在布氏硬度上提高了50个单位,在不损失钢板韧性的情况下延长了耐磨寿命。

Hardox550 is a kind of wear-resistant steel plate with average hardness of 550hbw. Its toughness is the same as hardox500. It is used in high wear occasions. It is mainly aimed at users and manufacturers using high manganese steel castings or wear-resistant steel plates with Brinell hardness of 500. When the HARDOX HARDOX 500 steel plate is upgraded to this product, the Brinell hardness is increased by 50 units, and the wear resistance life is prolonged without losing the toughness of the steel plate.hardox450耐磨板硬度等级 hardox450耐磨板用途(图1)

hardox600是世界上比较硬的耐磨钢板,硬度值达是600HBW。它一般应用于磨损极其严重的场合,并且主要用来替代铸钢、铬合金铸铁以及表面硬化金属。尽管它的硬度很高,我们还是能够对它进行机加工、焊接和切割。尽管hardox 600的硬度非常高,但它仍具有相当高的冲击韧性。

HARDOX HARDOX 600 is a hard wear-resistant steel plate in the world with a hardness value of 600hbw. It is generally used in severe wear cases, and mainly used to replace cast steel, chromium alloy cast iron and surface hardening metal. Despite its high hardness, we can machine, weld and cut it. Although HARDOX has a very high hardness of 600, it still has a high impact toughness.

1.hardox450是布氏硬度450HB的耐磨钢板,具有良好的冷弯性,主要应用于抗磨损工况。hardox450具备非常好的可焊性。

1. HARDOX HARDOX 450 is a wear-resistant steel plate with a Brinell hardness of 450hb. It has good cold bending property and is mainly used in wear resistant conditions. HARDOX 450 has very good weldability.

2.hardox450应用于自卸车车厢,集装箱,破碎机,筛板,入料器,给料漏斗,提升机,刃板,输送机,挖斗,刀板,齿轮,链轮等

2. HARDOX  450 is used in dump truck carriage, container, crusher, sieve plate, feeder, feeding hopper, elevator, blade, conveyor, bucket, cutter plate, gear, sprocket, etc

4.hardox450耐磨钢硬度:HBW425-475。 

4. Hardox450 HARDOX wear resistant steel hardness: hbw425-475. 

5.hardox450耐磨钢机械性能:屈服强度Re=1200MPa。抗拉强度Rm=1400MPa。延伸率A5=10%(20毫米厚度钢板典型值)。

5. The mechanical properties of hardox450 HARDOX wear-resistant steel are re = 1200Mpa. Tensile strength RM = 1400MPa. Elongation A5 = 10% (typical for 20 mm thick steel plate).

6.hardox450耐磨钢交货状态:淬火。

6. Hardox450 HARDOX wear resistant steel delivery status: quenched.

7.hardox450耐磨钢冲击韧性:试验温度:-40(-40F)℃。冲击功Charpy-V纵向=45J(20毫米厚度钢板典型值)。

7.Impact toughness of hardox450 HARDOX wear resistant steel: test temperature: - 40 (- 40F) ℃. Charpy-V longitudinal = 45j (typical value of 20 mm thick steel plate).

8.hardox450耐磨钢执行标准:EN 10 204 - 3.1。

8. Hardox450 HARDOX wear resistant steel executive standard: en 10204 - 3.1.

9.产品应用: 由于兼具高硬度、高强度以及高韧性,对于那些磨损严重的场合,hardox悍达耐磨板显然是理想之选。钢板的高耐磨性延长了自卸车车身、挖掘机的铲斗、破碎机以及类似设备的使用寿命。

9. Product application: due to its high hardness, high strength and high toughness, HARDOX hardplate is obviously the ideal choice for those occasions with severe wear. The high wear resistance of steel plate extends the service life of dump truck body, excavator bucket, crusher and similar equipment.

钢板的硬度是通过我们水淬火线上有效的淬火工艺获得的。这一方法既可获得较高的硬度,又可保持钢材中较低的合金成分。产出的耐磨板易于机加工、弯曲和焊接。 用途:自卸车车身,震动筛,进料斗,挖斗,刀板,铲斗,刮板运输机,齿轮等等。

The hardness of steel plate is obtained by effective quenching process on our water quenching line. This method can not only obtain higher hardness, but also keep lower alloy composition in steel. The wear plate produced is easy to machine, bend and weld. Application: dump truck body, vibrating screen, feeding hopper, bucket, cutter board, bucket, scraper conveyor, gear, etc.